SANDVIK22.9.3.LT1

FLUX CORED WIRE ELECTRODES

DATASHEET

Sandvik 22.9.3.L-T1 (2209L-T1) is a chromium-nickel-molybdenum-nitrogen flux core electrode for welding of for welding of 22-23%Cr duplex (ferritic-austenitic) stainless steels (e.g. Sandvik SAF 2205).

The electrode has excellent arc stability, low spatter and fast burn off rate. It is also characterized by improved moisture resistance, self-peeling slag and easy post weld finishing. Sandvik 22.9.3.L-T1 (2209L-T1) gives smooth uniform beads and works in any standard weld position.

STANDARDS

-ISO 14174:T2293NLPCM2 -AWS A5.22/ASMEA5.22:E2209-T1-1/T1-4 -Wnr: 1.4462

Product Approvals

-AWS

Please note that the Werkstoff Nr. corresponds to the base material of the grade.

CHEMICAL COMPOSITION (NOMINAL) %

Chemical composition (nominal) %

c

Si

Mn

Cr

Ni

Mo

N

0.03

0.47

1.15

22.9

9

3.2

0.16

The all-weld metal for Sandvik 22.9.3.L-T1 (2209L-T1) is ferritic-austenitic with a ferrite content of approximately 45 FN according to WRC-92.

APPLICATIONS

Sandvik 22.9.3.L-T1 (2209-T1) is used for welding steels of the following types:

ISO

1.4462, 1.4362, 1.4162, 1.4662,1.4460, 1.4417

ASTM

UNS S32205, S31803, S32304, S32101 ( S82441

Sandvik 22.9.3-T1 (2209-T1) is used for welding duplex and lean duplex stainless steels in service temperatures up to 280°C (536°F).

FORMS OF SUPPLY

Sandvik 22.9.3.L-T1 (2209-T1 > is supplied in wire of diameters 0.9,1.2, 1.6 mm (0.035, 0.047.1 門 6 in.).

MECHANICAL PROPERTIES Using Ar75%/C〇2 25%